I
PENGARUH KONSENTASI TOTAL TITRATABLE ALKALI TERHADAP PERSEN CAUSTICIZING EFFICIENCY DAN PERSEN SULFIDITY DI DALAM WHITE LIQUOR STORAGE PADA PROSES RECAUSTICIZING DI PT. TOBA PULP LESTARI, Tbk.
KARYA ILMIAH
ARRYE GENAP PARHUSIP 102401031
PROGRAM STUDI DIPLOMA 3 KIMIA DEPARTEMEN KIM IA FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SUMATERA UTARA MEDAN 2013
II
PENGARUH KONSENTRASI TOTAL TITRATABLE ALKALI TERHADAP PERSEN CAUSTICIZING EFFICIENCY DAN PERSEN SULFIDITY DI DALAM WHITE LIQUOR STORAGE PADA PROSES RECAUSTICIZING DI PT. TOBA PULP LESTARI, Tbk.
KARYA ILMIAH
Diajukan untuk melengkapi tugas dan memenuhi syarat memperoleh gelar Ahli Madya.
ARRYE GENAP PARHUSIP 102401031
PROGRAM STUDI DIPLOMA 3 KIMIA DEPARTEMEN KIM IA FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SUMATERA UTARA MEDAN 2013
III
PERSETUJUAN
Judul
: PENGARUH KONSENTRASI TOTAL TITRATABLE ALKALI TERHADAP PERSEN CAUSTICIZING EFFICIENCY DAN PERSEN SULFIDITY DI DALAM WHITELIQUOR STORAGE PADA PROSES RECAUSTICIZING DI PT. TOBA PULP LESTARI, Tbk. Kategori : KARYA ILMIAH Nama : ARRYE GENAP PARHUSIP Nomor Induk Mahasiswa : 102401031 Program Studi : DIPLOMA (D3) KIMIA Departement : KIMIA Fakultas : MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) UNIVERSITAS SUMATERA UTARA (USU) Disetujui di Medan, Juli 2013 Diketahui
Ketua Program studi D3 Kimia FMIPA USU
Pembimbing
Dra. EMMA ZAIDAR, M.Si NIP. 195512181987012001
Dr. YUNIARTI YUSAK, MS NIP. 194901271980022001
Mengetahui Ketua Departement Kimia FMIPA USU
Dr. RUMONDANG BULAN, MS NIP : 195408301985032001
IV
PERNYATAAN
PENGARUH KONSENTRASI TOTAL TITRATABLE ALKALI TERHADAP PERSEN CAUSTICIZING EFFICIENCY DAN PERSEN SULFIDITY DI DALAM WHITE LIQUOR STORAGE PADA PROSES RECAUSTICIZING DI PT. TOBA PULP LESTARI, Tbk.
KARYA ILMIAH
Saya mengakui bahwa karya ilmiah ini adalah hasil kerja saya sendiri, kecuali beberapa kutipan dan ringkasan yang masing-masing disebutkan sumbernya.
Medan,
Juli 2013
ARRYE GENAP PARHUSIP 102401031
V
PENGHARGAAN
Segala puji dan syukur penulis ucapkan kehadirat Tuhan yang Maha Esa, atas rahmat dan cinta kasih-Nya yang telah dilimpahkannya kepada kita semua, sehingga penulis dapat melaksanakan dan menyelesaikan Karya Ilmiah ini dengan judul Pengaruh Konsentrasi Total Titrable Alkali Terhadap Persen Causticizing Efficiency, dan Persen Sulfidity Di Dalam White Liquor Storage Pada Proses Recausticizing Di PT. Toba Pulp Lestari, Tbk sesuai dengan waktu yang telah ditentukan. Karya Ilmiah ini merupakan salah - satu syarat untuk menyelesaikan pendidikan Diploma - 3 Kimia Analis Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Sumatera Utara. Penulis juga menyadari bayak kekurangan dari Karya Ilmiah ini, maka dengan kerendahan hati penulis mengharapkan saran dan kritik yang sifatnya membangun dari berbagai pihak demi penyempurnaan Karya Ilmiah ini. Penulis juga menyadari Karya Ilmiah ini tersususn dan terselesaikan dengan baik karena ada campur tangan dari berbagai pihak yang mendukung penulis dalam meyelesaikan Karya Ilmiah ini, oleh karena itu penulis mengucapkan terimakasi kepada : 1. Orang tua tercinta Bapak Pdt . G. Parhusip dan Ibu S. Samosir yang mendukung dan memotivasi penulis dalam menyelesaikan menyelesaikan Karya Ilmiah ini. 2. Ibu Dr. Yuniarti Yusak, MS selaku dosen pembimbing, Ibu Dr. Rumondang Bulan Nasution, MS selaku ketua Departement Kimia Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Sumatera Utara, dan Ibu Dra. Emma Zaidar, M.Si selaku ketua jurusan D-3 Kimia Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Sumatera Utara yang banyak mengarahkan dan membantu penulis dalam menyelesaikan Karya Ilmiah ini. 3. Bapak Arlodis Nainggolan selaku pembimbing lapangan dan keluarga besar laboratorium PT. Toba Pulp Lestari, Tbk yang telah banyak memberikan sumbangan, pikiran, tenaga, dan waktu kepada penulis sewaktu penulis melaksanakan Praktek Kerja Lapangan. 4. Bapak Irwan Kelana Putra Selaku Learning & Dev. Centre Section Head, para staff di L&D Centre ( Ibu Yanthi Sormin, Bapak Derusman Purba ), dan bapak Jhonny Marpaung selaku staff di LP&C yang telah memberikan kesempatan kepada penulis untuk mengikuti Praktek Kerja Lapangan di PT. Toba Pulp Lestari, Tbk Parmaksian. 5. Dan yang terakhir buat teman-teman seperjuangan selama mengikuti Praktek Kerja Lapangan yaitu Linda Trisnawati Sembiring, Posma Tarida Tua Lumbangaol, Richard L. Manullang, Tiur Mawarni Parhusip (Itoku), Sri Rejeki Samosir (Ibanku), Silvia Julita Saragih. 6. Kepada teman – teman seperjuangan saya di kimia analis stambuk 2010 yang selalu memberi dukungan dan motivasi kepada penulis selama masa perkuliahan sampai penulisan Karya Ilmiah ini.
VI
Medan, Juli 2013 Penulis
ARRYE GENAP PARHUSIP
VII
ABSTRAK
White liquor adalah liquor yang diperoleh dari reaksi green liquor dengan kapur tohor (CaO), melalui proses recausticizing yang terjadi pada causticizer. Kandungan utamanya adalah Natrium hidroksida(NaOH), Natrium Sulfit(Na 2 S), dan Natrium karbonat(Na 2 CO 3 ) , dimana total dari jumlah senyawa tersebut dinyatakan dengan Total Titratable Alkali. White liquor inilah yang akan digunakan sebagai bahan utama pemasak kayu pada unit digester. Sebelum white liquor, digunakan perlu untuk mengontrol kualitas dari white liquor tersebut. Parameter yang dianalisa dalam white liquor adalah Total Alkali Aktif (TAA), persenCausticizing Efficiency (% CE), dan persen Sulfidity (%S). Dalam hal ini Target Total Alkali yang diinginkan adalah 93 g/l – 113 g/l, % Causticizing Efficiency adalah 72 – 83 %, dan % Sulfidity adalah 20 – 29 %, jika white liquor telah memenuhi target yang diharapkan, maka white liquor tersebut dapat digunakan sebagai bahan pemasak pada unit digester dalam proses produksi pulp.
VIII
TOTAL EFFECT OF CONCENTRATION TITRATABLE ALKALI TO PERCENT SULFIDITY AND PERCENT CAUSTICIZING EFFICIENCY IN WHITE LIQUOR STORAGE OF RECAUSTICIZING PROSES IN PT. TOBA PULP LESTARI, Tbk.
ABSTRACT
White liquor is a liquor obtained from the reaction of green liquor with calcium oxide (CaO), through a process that occurs in causticizer recausticizing. The content is primarily Sodium hydroxide (NaOH), Sodium sulphide (Na 2 S), and Sodium Carbonate (Na 2 CO 3 ) bit, where the total of the amount of the compound represented by the Total Titratable Alkali. White liquor is to be used as the main ingredient in the cooking wood in digester unit. Before the white liquor, should be used to control the quality of the white liquor. The parameters analyzed in the white liquor is Total Active Alkali (TAA), percent of Causticizing Efficiency (% CE), andpercent of Sulfidity (% S). In this case the Total Aktive Alkali desired target is 93 g / l - 113 g / l, percent Causticizing Efficiency is 72-83%, and percent Sulfidity is 20-29%, if the white liquor has met the expected target, then the white liquor can be used as a cooking ingredient in the units in the production process of pulp digester
IX
DAFTAR ISI
Halaman PERSETUJUAN..........................................................................................................iii PERNYATAAN...........................................................................................................iv PENGHARGAAN.........................................................................................................v ABSTRAK...................................................................................................................vii ABSTRACT...............................................................................................................viii DAFTAR ISI................................................................................................................ix DAFTAR TABEL.......................................................................................................xii
BAB 1. PENDAHULUAN............................................................................................1 1.1.Latar Belakang..............................................................................................1 1.2.Permasalahan................................................................................................5 1.3.Tujuan...........................................................................................................6 1.4.Mamfaat........................................................................................................6
BAB 2. TINJAUAN PUSTAKA..................................................................................7 2.1. Teori Umum Kayu.......................................................................................7 2.2. Sifat-Sifat Umum Kayu...............................................................................9 2.2.1. Sifat Fisik Kayu............................................................................9 2.2.2. Sifat Mekanik Kayu....................................................................12 2.2.3. Sifat-Sifat Kimia Kayu...............................................................13 2.3. Metode-Metode Pembuatan Pulp (Pulping Method).................................17 2.3.1. Metode Pembuatan Pulp Secara Mekanik (Mechanical Pulping)................................................................17 2.3.2. Metode Pembuatan Pulp Secara Semi Kimia (Semi Chemical Pulping).............................................................18 2.3.3. Metode Pembuatan Pulp Secara Kimia (Chemical Pulping)......18 2.4. Uraian Proses Sulphate/Kraft (Sulphate/Kraft Process)............................20
X
2.4.1. Tujuan Pembuatan Pulp Dengan Proses Kraft............................21 2.4.2. Larutan Pemasak.........................................................................22 2.5. Titrimetri....................................................................................................30 2.6. Larutan Baku/Standart...............................................................................32
BAB 3. BAHAN DAN METODE..............................................................................34 3.1. Alat dan Bahan...........................................................................................34 3.1.1. Alat.............................................................................................34 3.1.2. Bahan..........................................................................................34 3.2. Prosedur.....................................................................................................35
BAB 4. HASIL DAN PEMBAHASAN......................................................................36 4.1. Data............................................................................................................36 4.2. Perhitungan................................................................................................37 4.3. Pembahasan...............................................................................................40
BAB 5. KESIMPULAN DAN SARAN......................................................................42 5.1. Kesimpulan................................................................................................42 5.2. Saran..........................................................................................................42
DAFTAR PUSTAKA..................................................................................................43 LAMPIRAN
XI
DAFTAR TABEL
Halaman Tabel 1.1. Komposisi Typical Chemical antara hardwood dan softwood....................13 Tabel 1.2. Typical Pulp Yields of Components.............................................................23 Tabel 4.1. Hasil Analisa Total Titaratable Alkali, % Causticizing Efficiency, % Sulpidity dari White Liquor.........................................................................36