LAMPIRAN I - PEMERIKSAAN MATERIAL
ANALISA AYAKAN PASIR (ASTM C 136 - 84a)
Nama NIM Diuji oleh
Diameter ayakan (mm) 9.52 mm 4.75 mm 2.36 mm 1.18 mm 0.60 mm 0.30 mm 0.15 mm Pan Total
: Muhammad Fauzi : 10 0404 170 : Muhammad Fauzi
Berat Tertahan Berat sampel 1 (gram) 14,0 23,0 65,0 131,0 274,0 304,0 168,0 21,0 1000,0
Modulus Kehalusan (FM) Persyaratan pasir halus pasir sedang pasir kasar
=
Berat sampel 2 (gram) 15,0 20,0 60,0 130,0 276,0 300,0 170,0 29,0 1000,0
Total Weight (gram) 29,0 43,0 125,0 261,0 550,0 604,0 338,0 50,0 2000
266,30 100
=
Kumulatif (%) 1,45 2,15 6,25 13,05 27,50 30,20 16,90 2,50 100
Terthan (%) 1,45 3,60 9,85 22,90 50,40 80,60 97,50 100,00
Lolos (%) 98,55 96,40 90,15 77,10 49,60 19,40 2,50 0,00
2,66
2.2
Mengetahui, Asisten Laboratorium Beton
( Rahmadsyah Rangkuti )
Universitas Sumatera Utara
BERAT ISI PASIR
ASTM C 29/C 29M - 90
Nama NIM Diuji oleh
: Muhammad Fauzi : 10 0404 170 : Muhammad Fauzi
Suhu Ruangan Suhu Air Berat Bejana Berat Air Berat Isi Air Faktor Koreksi' Diamater maksimum agregat
(0C) (0C) (kg) (kg) (kg/m3)
28,00 26,00 0,46 1,86 996,77 535,90
(mm)
10,00
Berat Isi Sampel 1 Sampel 2 Total
Rojok 3,37 3,40 6,77
Longgar 3,15 3,20 6,35
Rata - rata
3,38
3,18
Berat Bersih (kg)
2,92
2,71
Berat Isi [kg/m3]
1564,83
1453,09
Mengetahui, Asisten laboratorium Beton ( Rahmadsyah Rangkuti )
Universitas Sumatera Utara
BERAT JENIS DAN ABSORBSI PASIR (ASTM C 128 - 88)
Nama NIM Diuji oleh
: Muhammad Fauzi : 10 0404 170 : Muhammad Fauzi Sample I
Sample II
Average
Berat pasir keadaan SSD (gram)
500,0
500,0
500,0
Berat pasir + air + piknometer (gram)
971,0
972,0
971,5
Berat pasir kering oven (gram)
488,0
490,0
489,0
Berat piknometer + air (gram)
671,0
672,0
671,5
Berat Jenis Kering
2,44
2,45
2,45
Berat Jenis SSD
2,50
2,50
2,50
Berat Jenis Jenuh Air
2,60
2,58
2,59
Absorbsi %
2,46
2,04
2,25
Mengetahui, Asisten laboratorium Beton
( Rahmadsyah Rangkuti )
Universitas Sumatera Utara
KADAR LUMPUR PASIR (PENCUCIAN AGREGAT DENGAN AYAKAN NO. 200) ASTM C 117 - 90
Nama NIM Diuji oleh
: Muhammad Fauzi : 10 0404 170 : Muhammad Fauzi
sampel 1
sampel 2
rata - rata
Berat Kering Mula-mula (gram)
500
500
500
Berat Kering Setelah Pencucian (gram)
497
496
496,5
3
4
3,5
0,6
0,8
0,7
Berat Lolos Ayakan No. 200 (gram) Persentase Kadar Lumpur (%)
Mengetahui, Asisten laboratorium Beton
Rahmadsyah Rangkuti
Universitas Sumatera Utara
PENGUJIAN CLAY LUMP PASIR KADAR LIAT DALAM AGREGAT HALUS
Nama NIM Diuji oleh
: Muhammad Fauzi : 10 0404 170 : Muhammad Fauzi
sampel 1
sampel 2
rata - rata
Berat Kering Hasil Pengujian Kadar Lumpur (gram)
497
496
496,5
Berat Kering Setelah Pencucian (gram)
495
495
495
2
1
1,5
0,40
0,20
0,30
Berat Lolos Ayakan No. 200 (gram) Persentase Kadar Lumpur (%)
Mengetahui, Asisten laboratorium Beton
Rahmadsyah Rangkuti
Universitas Sumatera Utara
PENGUJIAN COLORIMETRIC KANDUNGAN BAHAN ORGANIK AGREGAT HALUS
Nama NIM Diuji oleh
: Muhammad Fauzi : 10 0404 170 : Muhammad Fauzi
Keterangan
Sampel Lebih Terang
Perbandingan Terhadap Warna Standard Gardner
Sama
No. 3
Lebih Gelap
Mengetahui, Asisten laboratorium Beton
Rahmadsyah Rangkuti
Universitas Sumatera Utara
LAMPIRAN II - DATA BERAT ISI, ABSORBSI, DAN POROSITAS
1. BERAT ISI (KEADAAN SEIMBANG) NO.
KODE SAMPEL
BERAT KERING gram 9842 9898 9832 9874 9900
BERAT JENUH gram 10294 10352 10280 10351 10381
BERAT TERENDAM gram 5034 5041 5014 4981 5030
BERAT ISI kg/m³ 1865,49 1858,09 1861,47 1833,22 1844,57
1 2 3 4 5
0% 0% 0% 0% 0%
1 2 3 4 5
rata - rata 15% 15% 15% 15% 15%
9869,2 9785 9840 9814 9777 9840
10331,6 10260 10325 10321 10250 10351
5020 4983 4993 4930 4962 4985
1852,57 1848,71 1839,92 1814,98 1843,36 1828,27
1 2 3 4 5
rata - rata 20% 20% 20% 20% 20%
9811,2 9825 9759 9800 9768 9819
10301,4 10340 10248 10311 10256 10314
4970,6 4965 4952 4919 4968 4976
1835,05 1822,42 1837,18 1812,05 1841,66 1833,93
1 2 3 4 5
rata - rata 25% 25% 25% 25% 25%
9794,2 9808 9801 9758 9754 9786
10293,8 10294 10295 10260 10258 10301
4956 4946 4940 4934 4937 4948
1829,45 1828,45 1824,76 1826,65 1827,61 1822,65
rata - rata
9781,4
10281,6
4941
1826,03
Universitas Sumatera Utara
2. ABSORBSI KODE NO. SAMPEL
MASSA BASAH gram 10294 10352 10280 10351 10381
MASSA KERING gram 9842 9898 9832 9874 9900
ABSORBSI % 4,59 4,59 4,56 4,83 4,86
1 2 3 4 5
0% 0% 0% 0% 0%
1 2 3 4 5
rata - rata 15% 15% 15% 15% 15%
10331,6 10260 10325 10321 10250 10351
9869,2 9785 9840 9814 9777 9840
4,69 4,85 4,93 5,17 4,84 5,19
1 2 3 4 5
rata - rata 20% 20% 20% 20% 20%
10301,4 10340 10248 10311 10256 10314
9811,2 9825 9759 9800 9768 9819
5,00 5,24 5,01 5,21 5,00 5,04
1 2 3 4 5
rata - rata 25% 25% 25% 25% 25%
10293,8 10294 10295 10260 10258 10301
9794,2 9808 9801 9758 9754 9786
5,10 4,96 5,04 5,14 5,17 5,26
rata - rata
10281,6
9781,4
5,11
Universitas Sumatera Utara
3. POROSITAS
0% 0% 0% 0% 0%
MASSA BASAH gram 10294 10352 10280 10351 10381
MASSA KERING gram 9842 9898 9832 9874 9900
VOLUME BENDA UJI cm³ 5298,75 5298,75 5298,75 5298,75 5298,75
POROSITAS % 8,530 8,568 8,455 9,002 9,078
1 2 3 4 5
rata - rata 15% 15% 15% 15% 15%
10331,6 10260 10325 10321 10250 10351
9869,2 9785 9840 9814 9777 9840
5298,75 5298,75 5298,75 5298,75 5298,75 5298,75
8,727 8,964 9,153 9,568 8,927 9,644
1 2 3 4 5
rata - rata 20% 20% 20% 20% 20%
10301,4 10340 10248 10311 10256 10314
9811,2 9825 9759 9800 9768 9819
5298,75 5298,75 5298,75 5298,75 5298,75 5298,75
9,251 9,719 9,229 9,644 9,210 9,342
1 2 3 4 5
rata - rata 25% 25% 25% 25% 25%
10293,8 10294 10295 10260 10258 10301
9794,2 9808 9801 9758 9754 9786
5298,75 5298,75 5298,75 5298,75 5298,75 5298,75
9,429 9,172 9,323 9,474 9,512 9,719
rata - rata
10281,6
9781,4
5298,75
9,440
NO.
KODE SAMPEL
1 2 3 4 5
Universitas Sumatera Utara
LAMPIRAN III - KUAT TEKAN BETON
No.
Nomor Benda Uji
1
Variasi 1
2
Variasi 1
3
Variasi 1
4
Variasi 1
5
Variasi 1
1
Variasi 2
2
Variasi 2
3
Variasi 2
4
Variasi 2
5
Variasi 2
Subs. Fly Ash (%) 0 0 0 0 0
15 15 15 15 15
Tanggal cetak
uji
27-Agust-14 27-Agust-14 27-Agust-14 27-Agust-14 27-Agust-14
24-Sep-14 24-Sep-14 24-Sep-14 24-Sep-14 24-Sep-14 Rata - rata
27-Agust-14 27-Agust-14 27-Agust-14 27-Agust-14 27-Agust-14
Umur Berat uji (hari) (kg) 9,842 28 9,898 28 9,832 28 9,874 28 9,900 28
Beban Tekan (kN) 280,0 292,0 274,0 280,0 292,0
Kuat Tekan (MPa) 15,85 16,53 15,51 15,85 16,53
9,87
283,60
16,06
9,787 9,843 9,777 9,819 9,845
270,0 284,0 262,0 276,0 266,0
15,29 16,08 14,83 15,63 15,06
9,81
271,60
15,38
24-Sep-14 24-Sep-14 24-Sep-14 24-Sep-14 24-Sep-14 Rata - rata
28 28 28 28 28
1 2 3 4 5
Variasi 3 Variasi 3 Variasi 3 Variasi 3 Variasi 3
20 20 20 20 20
27-Agust-14 27-Agust-14 27-Agust-14 27-Agust-14 27-Agust-14
24-Sep-14 24-Sep-14 24-Sep-14 24-Sep-14 24-Sep-14 Rata - rata
28 28 28 28 28
9,767 240,0 9,823 238,0 9,757 264,0 9,799 278,0 9,825 240,0 9,79 252,00
13,59 13,47 14,95 15,74 13,59 14,27
1 2 3 4 5
Variasi 4 Variasi 4 Variasi 4 Variasi 4 Variasi 4
25 25 25 25 25
27-Agust-14 27-Agust-14 27-Agust-14 27-Agust-14 27-Agust-14
24-Sep-14 24-Sep-14 24-Sep-14 24-Sep-14 24-Sep-14 Rata - rata
28 28 28 28 28
9,754 9,810 9,744 9,786 9,812
198,0 226,0 210,0 228,0 222,0
11,21 12,80 11,89 12,91 12,57
9,78
216,80
12,27
Universitas Sumatera Utara
LAMPIRAN IV - KUAT TEKAN BETON Variasi Substitusi Fly Ash
0%
Rata - rata
15%
Rata - rata
20%
Rata - rata
25%
Rata - rata
Beban Rekah (kN) 112 122 98 112 130 114,80 108 112 90 100 96 101,20 86 78 80 58 76 75,60 48 62 58 60 50 55,60
Tegangan Rekah Beton (MPa) D
¾D
½D
¼D
1,5852795 1,7268224 1,3871196 1,5852795 1,8400566 1,62 1,5286624 1,5852795 1,2738854 1,4154282 1,358811 1,43 1,2172682 1,104034 1,1323425 0,8209483 1,0757254 1,07 0,6794055 0,8775655 0,8209483 0,8492569 0,7077141 0,79
2,1137061 2,3024298 1,8494928 2,1137061 2,4534088 2,17 2,0382166 2,1137061 1,6985138 1,8872376 1,8117481 1,91 1,6230243 1,4720453 1,50979 1,0945978 1,4343005 1,43 0,905874 1,1700873 1,0945978 1,1323425 0,9436188 1,05
3,1705591 3,4536447 2,7742392 3,1705591 3,6801132 3,25 3,0573248 3,1705591 2,5477707 2,8308563 2,7176221 2,86 2,4345364 2,2080679 2,2646851 1,6418967 2,1514508 2,14 1,358811 1,7551309 1,6418967 1,6985138 1,4154282 1,57
6,3411182 6,9072895 5,5484784 6,3411182 7,3602265 6,50 6,1146497 6,3411182 5,0955414 5,6617127 5,4352442 5,73 4,8690729 4,4161359 4,5293701 3,2837933 4,3029016 4,28 2,7176221 3,5102619 3,2837933 3,3970276 2,8308563 3,15
Tegangan Rekah (MPa) 3,302665723 3,597546591 2,889832508 3,302665723 3,833451286 3,39 3,184713376 3,302665723 2,653927813 2,948808681 2,830856334 2,98 2,535975466 2,300070771 2,359046945 1,710309035 2,241094598 2,23 1,415428167 1,828261382 1,710309035 1,769285209 1,474404341 1,64
Universitas Sumatera Utara
LAMPIRAN V - DOKUMENTASI
Gambar 1. Fly Ash
Gambar 2. Bubuk Kertas
Universitas Sumatera Utara
Gambar 3. Penuangan bahan dengan substitusi fly ash
Gambar 4. Penuangan bahan bubur kertas
Universitas Sumatera Utara
Gambar 5. Pengujian slump
Gambar 6. Penuangan adukan beton kertas dengan substitusi fly ash
Universitas Sumatera Utara
Gambar 7. Pemadatan benda uji dengan vibrator
Gambar 8. Benda uji yang telah di cetak
Universitas Sumatera Utara
Gambar 9. Penimbangan berat benda uji terendam
Gambar 10. Penimbangan berat benda uji
Universitas Sumatera Utara
Gambar 11. Pengujian kuat tekan beton kertas
Gambar 12. Benda uji setelah diuji
Universitas Sumatera Utara
Gambar 13. Pengujian kuat tarik belah
Gambar 14. Benda uji setelah diuji tarik belah
Universitas Sumatera Utara